Materiales: Metales y plasticos

Metales

MaterialQ235
Yield≥235
Tensile375-500
HardnessHB 120 +/- 40
GB StandardGB/T 700-2006
MaterialQ345B
Yield≥345
Tensile490-675
HardnessHB 120 +/- 40
GB StandardGB/T 1591-2008
MaterialSAPH440
Yield≥305
Tensile≥440
HardnessHB 80 +/- 30
GB StandardQ/BQB 310-2009
MaterialAluminum 1060
Yield≥35
Tensile≥75
HardnessHB 26 +/- 5
GB StandardGB/T 3190-2008
MaterialAluminum 6061 T5
Yield≥170
Tensile≥250
HardnessHB 30 +/- 5
GB StandardGB/T 3190-2008
MaterialAluminum 6061 T6
Yield≥260
Tensile≥276
HardnessHV 15-18
GB StandardGB/T 3190-2008
MaterialAluminum 6063 T5
Yield≥170
Tensile≥205
HardnessHB 25 +/- 5
GB StandardGB/T 3190-2008
MaterialAluminum 5052 H32
Yield≥70
Tensile210-260
HardnessHV 11 +/- 2
GB StandardGB/T 3190-2008
MaterialStainless Steel SS301
Yield≥205
Tensile≥520
HardnessHB 76-187
GB StandardGB/T 8170-2008
MaterialStainless Steel SS304
Yield≥205
Tensile≥520
HardnessHB 76-187
GB StandardGB/T 24511-2009
MaterialStainless Steel SS316
Yield≥205
Tensile≥520
HardnessHB 76-187
GB StandardGB/T 24511-2009
Material65 Mn
Yield≥785
Tensile≥980
HardnessHB 190-340
GB StandardGB/T 1222-2007
MaterialSGCC
Yield≥200
Tensile≥380
HardnessHB 50-65
GB StandardJIS-G3302
MaterialSPCC
Yield≥210
Tensile≥350
HardnessHB 65-85
GB StandardJIS-G3141-2009

Plásticos

MaterialPC
Tensile Strength (MPa)55-75
Elongation at Break (%)100-150
Surface Hardness (Rockwell)RM 70
MaterialPMMA
Tensile Strength (MPa)80
Elongation at Break (%)2.5-4
Surface Hardness (Rockwell)M92-100
MaterialABS V0
Tensile Strength (MPa)
Elongation at Break (%)
Surface Hardness (Rockwell)
MaterialABS
Tensile Strength (MPa)41-45
Elongation at Break (%)45
Surface Hardness (Rockwell)R100-110
MaterialPA66
Tensile Strength (MPa)82
Elongation at Break (%)M89
Surface Hardness (Rockwell)M89
MaterialPA6
Tensile Strength (MPa)78
Elongation at Break (%)M82
Surface Hardness (Rockwell)M82
MaterialPA 66 +30%GFR
Tensile Strength (MPa)160-210
Elongation at Break (%)5
Surface Hardness (Rockwell)M100
MaterialPP
Tensile Strength (MPa)26
Elongation at Break (%)150-300
Surface Hardness (Rockwell)R80-100
MaterialPE
Tensile Strength (MPa)20-40
Elongation at Break (%)350
Surface Hardness (Rockwell)R50-70
MaterialHDPE
Tensile Strength (MPa)15-40
Elongation at Break (%)
Surface Hardness (Rockwell)D60-73-Shore